Makrolon® Rx1805

Grades/医疗设备



性能

流变性能




MVR (300 °C/1.2 kg) 6.0 cm3/10 min; medical devices; high lipid resistance; suitable for sterilization
with high-energy radiation; biocompatible according to many ISO 10993- 1 test requirements; high
viscosity; injection molding - melt temperature 280 - 320 °C; transparent parts for medical devices
ISO 7391-PC,M,(,,)-09-9
测试条件
-


C 熔融指数 (体积) 300 °C; 1.2 kg cm3/10 min ISO 1133 6.0
C 成型收缩率, 流动方向 60x60x2 mm; 500 bar % ISO 294-4 0.7
C 成型收缩率, 垂直流动方向 60x60x2 mm; 500 bar % ISO 294-4 0.7
C 成型收缩率, 流动方向/垂直流动方向 Value range based on general
practical experience % b.o. ISO 2577 0.6 - 0.8
C 熔融指数 (质量) 300 °C; 1.2 kg g/10 min ISO 1133 6.5
机械性能
C 抗拉模量 1 mm/min MPa ISO 527-1,-2 2400
C 屈服应力 50 mm/min MPa ISO 527-1,-2 67
C 屈服应变 50 mm/min % ISO 527-1,-2 6.3
C 名义断裂拉伸应变 50 mm/min % ISO 527-1,-2 > 50
C 断裂应力 50 mm/min MPa ISO 527-1,-2 75
C 断裂应变 50 mm/min % b.o. ISO 527-1,-2 130
C 弯曲模量 2 mm/min MPa ISO 178 2400
C 弯曲强度 2 mm/min MPa ISO 178 98
C 弯曲强度下的弯曲应变 2 mm/min % ISO 178 7.1
C 3.5%应弯时的弯曲应力 2 mm/min MPa ISO 178 73
C Charpy 冲击强度 23 °C kJ/m2 ISO 179-1eU N
C Charpy 冲击强度 -30 °C kJ/m2 ISO 179-1eU N
C Charpy 冲击强度 -60 °C kJ/m2 ISO 179-1eU N
C Charpy 缺口冲击强度 23 °C; 3 mm kJ/m2 ISO 7391/b.o. ISO
179-1eA 80P
C Charpy 缺口冲击强度 -30 °C; 3 mm kJ/m2 ISO 7391/b.o. ISO
179-1eA 16C
C Izod 缺口冲击强度 23 °C; 3 mm kJ/m2 ISO 7391/b.o. ISO
180-A 70P
C Izod 缺口冲击强度 -30 °C; 3 mm kJ/m2 ISO 7391/b.o. ISO
180-A 15C
C ~大穿透力 23 °C N ISO 6603-2 5700
C ~大穿透力 -30 °C N ISO 6603-2 6600
C 穿透能量 23 °C J ISO 6603-2 65
C 穿透能量 -30 °C J ISO 6603-2 70
C 球压硬度 N/mm2 ISO 2039-1 114






产品名称：供应科思创PC RX1805 451118透明拜耳聚碳酸酯
产品手机链接：http://m.vooec.com/product_224452140.html
产品网站链接：http://www.vooec.com/cpshow_224452140/