日本大科能Techno ABS、330C
特点：高流动 TECHNO ABS 330C
Property "Test
Method" Unit
"High Flow
TECHNO ABS
330C (38B)"
Tensile Strength ISO 527 M Pa 47
Flexural Strength ISO 178 M Pa 73
Flexural Modulus ISO 178 M Pa 2,260
Charpy Impact ISO 179 KJ/m2 9
Rockwell Hardness ISO 2039 - R108
Melt Mass Flow Rate ISO 1133 g/10Min. Test condition "56.0
220°C,98N"
Temp. of Deflection "(U ISO 75 d)
nder Loa" °C 80
Density ISO 1183 - 1.05
Molding Shrinkage ISO 294-4 "Low
High" "0.30
0.60"
Flammability UL94 "Min. Thick
(mm) Flame Class
color" "HB
ALL"

同时在售日本大科能Techno ABS其他牌号：
ABS TECHNO F1350(D4)
ABS TECHNO F1350G10
ABS TECHNO F1384
ABS TECHNO F5170
ABS TECHNO F5330
ABS TECHNO F5330G10
ABS TECHNO F5330G20
ABS TECHNO F5330G30
ABS TECHNO F5450
ABS TECHNO F5450 W
ABS TECHNO F5451G10
ABS TECHNO F5451G20
ABS TECHNO F5451G30
ABS TECHNO F5452
ABS TECHNO F5456
ABS TECHNO F7850
ABS TECHNO H530L
ABS TECHNO H571
ABS TECHNO H593
ABS TECHNO H596
ABS TECHNO H630
ABS TECHNO H814
ABS TECHNO HZTFXST
ABS+PC TECHNO R5405A
ABS+PC TECHNO R5601A
ABS+PC TECHNO R5601B
ABS TECHNO R760
ABS TECHNO R790
ABS TECHNO R790P
ABS TECHNO S1708C
ABS TECHNO TFX-SBT3
ABS TECHNO TFX-STG
ABS TECHNO ZF5551

由于ABS树脂具有吸湿性，预ABS造粒干燥是要实现良好的成型外观。虽然情况将取决于干燥的被使用，等性能或规格不同，不足够的干燥温度和干燥时间等，可能会导致较差的外观（银纹，等）。在一般情况下，温度5～10°C高于ISO负荷热畸变温度（即，温度5到10°C低于ASTM负荷热畸变温度）相应等级是适宜的干燥温度（实际温度），在温度超过它可能导致干燥等干燥料斗堵塞，等在干燥的实际温度低于ISO负荷热畸变温度的情况下，它可能会导致在长的干燥时间尽管可怜的样子

产品名称：330C 大科能ABS
产品手机链接：http://m.vooec.com/trade_89679053.html
产品网站链接：http://www.vooec.com/sjshow_89679053/